Differences between ASTM D790 and ISO 178
ASTM D790 is very similar to ISO 178, though it differs in several key points:
What Does it Measure?
- ISO 178 requires the use of either a deflectometer or compliance correction in order to determine modulus. In ASTM D790, this is only a recommendation, and modulus can be calculated by crosshead displacement alone.
- Preferred specimen sizes are different, and because test speed is dependent on specimen depth, test speeds between the standards may vary. The preferred depth of ASTM D790 specimens is 3.2 mm. The preferred depth for ISO 178 specimens is 4 mm.
- ASTM D790 allows only one test speed, whereas ISO 178 allows a second (faster) test speed to be used after modulus is measured.
ASTM D790 measures the flexural properties of a material while under a bending strain or deflection. This test is conducted on a universal testing system using a three-point bend fixture at a rate proportional to the depth of the specimen. ASTM D790 testing is used to determine the following mechanical properties:
- Tangent modulus: Also known as flexural modulus, this is the slope of the initial linear portion of the load deflection curve and is a measurement of the material's stiffness.
- Secant modulus: The slope between the origin and a predefined point on the load deflection curve.
- Chord modulus: The slope between two predefined points on the load deflection curve.
- Flexural strength: The maximum flexural stress obtained during a bend test.
- Flexural stress at break: The flexural stress at which a specimen breaks during a bend test. For some materials, the specimen breaks before a yield point, in which case the flexural strength equals the flexural stress at break.
ASTM D790 describes two different test procedures intended for different types of material. Procedure A, which is the preferred method, employs a strain rate of 0.01 mm/mm/min. Procedure B employs a strain rate of 0.10 mm/mm/min and is intended for materials that may not break at 5% strain if tested at the lower rate. ASTM D790 allows strain measurement to be taken from either crosshead displacement or the readings of an extensometer, described as Type 1 and Type 2 testing, respectively.
The required test speed for ASTM D790 is expressed as a function of specimen support span, specimen depth, and strain rate. Bluehill® Universal's Expression Builder allows users to input test speed as a function instead of as a static number. After the test operator enters the specimen measurements, the software will automatically modify the test speed according to the equation.
ASTM D790 testing can be done on either a tabletop or floor model universal testing machine with a variety of accessories that can be configured to optimize your testing. Because every laboratory has different needs, several different system configurations are available.
A sample basic configuration can be seen below. This test setup includes a 3400 Series test system with a 3-point bend fixture and no extensometer, meaning that strain in this case must be measured by crosshead displacement (Type 1 testing). Whenever strain is measured via crosshead displacement, compliance correction is recommended, though not required. 3400 series test frames can also be used in conjunction with extensometry for Type 2 testing.