Creep and Stress-Relaxation Test

What is a Creep Test?

A creep test, sometimes referred to as a stress-relaxation test, is used to determine the amount of deformation a material experiences over time while under a continuous tensile or compressive load at a constant temperature. Creep tests are fundamental for materials that are needed to withstand certain operation temperatures under load. For materials such as metals or alloys, their material properties change significantly at higher or lower temperatures. By examining the results from a creep test, engineers can determine a material's expected deformation and avoid failure when designing new systems for different environmental conditions. Creep tests are commonly performed on the following components and materials:

  • Metal Working
  • Springs
  • Soldered Joints
  • High-Temperature Materials

How to Perform a Creep Test?

To determine creep properties, a material is subjected to prolonged constant tension or compression loading at constant elevated temperature. While testing, the material's deformation is recorded at specific time intervals and overall data is plotted on a creep vs time diagram. The slope at any point on this curve is known as the creep rate, in which units are expressed in terms of in/in/hr or percent(%) elongation/hr. Maintaining a constant temperature during a creep test is critical due to the possible thermal expansion or shrinkage of the material.

Three Stages of Creep Testing 

Specimens pass through three different stages during a creep test. The first stage is primary creep, where the creep rate begins by rising quickly and then slows down and decreases. The secondary stage is where the creep rate remains fairly uniform. During the tertiary stage, when the specimen is expected to reach its breaking point, the creep rate is much steeper than it is in the secondary stage, culminating in specimen failure. If failure occurs, the time for rupture is recorded. If a specimen does not fracture within the creep test period, creep recovery may be measured.

Some examples of standards that require creep testing are ASTM E139, ASTM D2290, ASTM D2291, and ASTM D2294. For more details on testing procedures, please refer to these standards. 

How to Determine Stress-Relaxation?

To determine the stress-relaxation of a material, the specimen is deformed a given amount and decrease in stress is recorded over prolonged period of exposure at constant elevated temperature. The stress-relaxation rate is the slope of the curve at any point.

creep test

 

Related Content

Serie 3400: soluciones de ensayo asequibles

Sistemas de ensayo universales Serie 3400 de Instron para ensayos de tracción, compresión, doblado y otros materiales.

Catálogo de sistemas de ensayo Serie 6800 Premier

Los sistemas de ensayo universales Serie 6800 de Instron proporcionan una precisión y fiabilidad sin igual. Construida sobre una arquitectura de sistema Operator Protect pendiente de patente, con un kit Smart-Close totalmente nuevo y funciones de mitigación de colisiones, la Serie 6800 hace que los ensayos de materiales sean más sencillos, limpios y seguros que nunca.

Catálogo de Bluehill Universal

El software Bluehill Universal está diseñado desde el principio para una interacción táctil y una experiencia de usuario intuitiva. Descubre ensayos más sencillos y limpios con funciones como métodos de ensayo precargados, QuickTest en segundos, exportación de datos mejorada e Instron Connect, una nueva función que proporciona un enlace de comunicación directa con el servicio. Los usuarios de versiones anteriores del software, como Bluehill 2 y Bluehill 3, pueden actualizarse fácilmente a la última versión de Bluehill.

Contacto

Contacto

Para obtener más información sobre nuestra industria y nuestras soluciones de pruebas, póngase en contacto con nosotros. Nuestros equipos de atención al cliente están listos para ayudarle.