ISO 13001 and ASTM D3479 Improving Throughput in Composites Fatigue Tests

The challenge

In recent years, composites fatigue testing has rapidly moved from a research interest to a critical commercial requirement, but the cost - in terms of machine time - remains a significant challenge to commercial testing The wind energy industry has led this demand, but aerospace and automotive sectors are defining their own needs in this area and fatigue performance is expected to become an additional qualification requirement for their composite materials and assemblies.

Cyclic loading of composites dissipates a considerable amount of energy, which results in “self-heating” of specimens. Not only can this cause specimen temperature to rise by more than 20 °C in the wrong test conditions, but this varies during the course of a test, and is rarely repeatable from one specimen to the next. Standard practice demands a single low frequency (typically 3 to 5 Hz) for all tests in order to avoid overheating, but that means very long and expensive test schedules.

Specimen Self Heating Control

Temperature has a major effect on results since the performance of these materials is far more temperature sensitive than that of metals. Unfortunately, the fact that specimens generate heat internally means that there is always an offset from the surrounding environment, so temperature rise is not actually controlled even when working in a chamber. In response to this demand, Instron® developed a unique control solution that typically gives more than a 25% time saving for a composite S-N dataset and can maintain specimen temperature to within ± 0.5 °C of a specified target.

 

 

Our Solution

Specimen Self-Heating Control in WaveMatrix2 dynamic test software accepts an input of specimen temperature, which is used in a sophisticated outer-loop control of test frequency*. The user sets the target test temperature and the system then automatically adjusts the live test frequency (within user-specified limits) to achieve it. This means that at low stress levels, where each specimen survives millions of cycles, the frequency can be increased to greatly reduce the test time. Conversely, at high stress levels (where each test is several orders of magnitude shorter) the frequency must often be reduced to prevent excessive heating, but this has little effect on the overall time for the S-N dataset.

Instron asked the UK National Composites Certification and Evaluation Facility at Manchester University (NCCEF) to assess the comparability of results by producing an S-N data set using their standard method followed by a complete repetition on the same batch of material using Specimen Self-Heating Control.

In two separate trials on commercial epoxy pre-preg materials with carbon fiber and e-glass fibre reinforcement (respectively), NCCEF found that the logarithmic data fitting coefficients were almost identical and that specimen temperature variation was reduced from ± 4 °C during a test to a range of less than ± 0.5 °C. On the carbon fiber reinforced material, the batch time was reduced by 15 machine-days on a total time of 55 days.

For the test laboratory struggling to fulfill demand for composites S-N curve generation, Specimen Self-Heating control offers exceptional value – the price of this small software extension can enable each machine to handle over 35% more tests.

*Thermocouples or non-contact transducers can be used.



Related Content

Catálogo de ElectroPuls®

Los instrumentos ElectroPuls son sistemas avanzados de ensayo electrodinámico para la realización de pruebas dinámicas y estáticas de materiales y componentes. Alimentados totalmente por una red monofásica, cuentan con la última tecnología para ensayos y otras muchas funciones orientadas al usuario.

Catálogo WaveMatrix2

WaveMatrix2 es un software inteligente diseñado para los ensayos de fatiga y dinámicos de materiales y componentes. Ofrece flexibilidad: realiza todo tipo de ensayos, desde una simple rampa estática hasta formas de onda cíclicas y complejas pruebas multiaxiales. El entorno altamente visual, con pantallas tabulares integradas, estructuras de menú claras, vista previa de ensayos matriciales basados en el tiempo y un espacio de trabajo de ensayos en vivo configurable, está diseñado para ser intuitivo y fiable. Ofrece varias funciones inteligentes, como la reducción de datos y la organización de proyectos integrada, diseñadas para simplificar tus ensayos.

Control de autocalentamiento de muestras WaveMatrix2

Aumenta el rendimiento y la calidad de tus ensayos de materiales compuestos y polímeros optimizando su frecuencia con el control de autocalentamiento de muestras. Este potente complemento es específico para el software WaveMatrix2. Los materiales compuestos y otros materiales son propensos a calentarse de manera excesiva durante la carga cíclica, pero su rendimiento también muestra una fuerte dependencia de la temperatura. Esto suele conllevar la realización de ensayos de fatiga a frecuencias muy bajas con el fin de reducir al mínimo el calentamiento de las muestras y la consiguiente degradación de las propiedades mecánicas. Una prueba para un único conjunto de datos S/N podría suponer semanas de tiempo de máquina. El control de autocalentamiento de muestras reduce de manera significativa este asunto, a la vez que proporciona una confianza antes inalcanzable en la temperatura del ensayo. Este sistema patentado alcanza y mantiene la temperatura especificada del ensayo variando la frecuencia en respuesta a la entrada de temperatura de la muestra.