Hardness Test
Simply stated, hardness is the resistance of a material to permanent indentation. It is important to recognize that hardness is an empirical test and therefore hardness is not a material property. This is because there are several different hardness tests that will each determine a different hardness value for the same piece of material. Therefore, hardness is test method dependent and every test result has to have a label identifying the test method used.Hardness is, however, used extensively to characterize materials and to determine if they are suitable for their intended use. All of the hardness tests described in this section involve the use of a specifically shaped indenter, significantly harder than the test sample, that is pressed into the surface of the sample using a specific force. Either the depth or size of the indent is measured to determine a hardness value.
Why Use a Hardness Test?
- Easy to perform
- Quick - 1 to 30 seconds
- Relatively inexpensive
- Non-destructive
- Finished parts can be tested - but not ruined
- Virtually any size and shape can be tested
- Practical QC device - incoming, outgoing
The most common uses for hardness tests is to verify the heat treatment of a part and to determine if a material has the properties necessary for its intended use. Establishing a correlation between the hardness result and the desired material property allows this, making hardness tests very useful in industrial and R&D applications.
Hardness Scales
- Brinell - HB
- Knoop - HK
- Rockwell - HR
- Shore - HS
- Vickers - HV
Each of these scales involve the use of a specifically shaped diamond, carbide or hardened steel indenter pressed into the material with a known force using a defined test procedure. The hardness values are determined by measuring either the depth of indenter penetration or the size of the resultant indent. All of the scales are arranged so that the hardness values determined increase as the material gets harder. The hardness values are reported using the proper symbol, HR, HV, HK, etc. indicating the test scale performed.
Five Determining Factors
The following five factors can be used to determine the correct hardness test for your application.
- Material - grain size, metal, rubber, etc.
- Approximate Hardness - hardened steel, rubber, etc.
- Shape - thickness, size, etc.
- Heat Treatment – through or casehardened, annealed, etc.
- Production Requirements - sample or 100%
Solutions d'essais abordables - La série 3400
Systèmes d'essais universels Instron série 3400 pour les essais de traction, de compression, de flexion et autres essais de propriété des matériaux.
Série 6800 Systèmes d'essai universels
Les systèmes d'essais universels Instron série 6800 offrent une précision et une fiabilité inégalées. Construit sur une architecture système Operator Protect en instance de brevet avec un tout nouveau kit de régulation d’air Smart-Close et des fonctions d’atténuation des collisions, la série 6800 rend les essais de matériaux plus simples, plus intelligents et plus sûrs que jamais.
Brochure Bluehill Universal
Le logiciel Bluehill Universal est intégralement conçu pour une interaction tactile et une expérience utilisateur intuitive. Vous découvrirez que les essais deviennent plus simples et plus intelligents grâce à des fonctionnalités, telles que les méthodes d’essais préconfigurées, le QuickTest fait en quelques secondes, l’exportation de données optimisée et Instron Connect - une nouvelle fonctionnalité qui fournit un lien de communication direct avec le service technique. Les utilisateurs des versions précédentes du logiciel, telles que Bluehill 2 et Bluehill 3, peuvent facilement faire la mise à jour à la toute dernière version de Bluehill.
Nous contacter
Contactez-nous pour en savoir plus sur notre industrie et nos solutions d’essais. Nos équipes d’assistance à la clientèle et de service sont à votre disposition pour vous aider.