ASTM A615 - Standard Specification for Deformed and Plain Carbon-Steel Bars for Concrete Reinforcement
Steel reinforcing bars are designed to absorb the stress and weight of concrete structures such as bridges and buildings. ASTM D615 is a testing standard that provides dimensional, chemical, and physical requirements for plain and deformed carbon steel bars manufactured for concrete reinforcement. Deformed bars include surface protrusions to prevent longitudinal movement after being placed in concrete, while plain bars are smooth sided. These products may be supplied in cut lengths or coils, and are engineered for the express purpose of building and construction.
While ASTM A615 references ASTM A370 and ASTM E290 for tensile and bend testing respectively, this standard includes specific procedures relevant to performing these tests on plain and deformed bar. These tests are performed in order to determine physical properties such as strength, elongation, and satisfactory surface condition after bending. Notably, bars produced in accordance with ASTM A706/A706M are also considered to be in conformance to this standard.
| ASTM A615 Test Setup | |
|---|---|
|
6800 Series floor model |
|
|
Bluehill Universal software |
|
|
2580 Series load cell |
|
| Hydraulic wedge grips | |
TEST CONTROL
Testing to ASTM A615 includes 5 basic regions including pretest, preload, elastic region, yielding, and plastic region.
Pretest
During pretest it is important to ensure that the proper grips are installed and test opening adjustments are made. Prior to installing the specimen, the force (load) measurement should be set zero. Once the specimen is loaded into the system, the force should NOT undergo any further “zeroing” as this will affect the test results. If using a manual extensometer for measuring strain, it should be properly attached to the specimen with the knife edges at the instrument’s gauge length. The strain measurement should then be set to zero prior to loading the specimen.
Preload
The preloading stage is used to apply a minimal preload (<5% of expected yield strength) to the specimen in order to properly seat it in the grips and also to aid in pulling the specimen straight prior to testing. A plot of stress or force versus crosshead or actuator displacement will typically show significant displacement for a minimal increase in load due to the grips and load string pulling tight (taking up system compliance). If a preload is not applied and an extensometer is being used, many rebar specimens will show negative strain at the beginning of the test as the specimen straightens. Because of this and/or system compliance, the data during the preloading portion of the test is often ignored or not recorded on the stress-strain graph.
On servo-controlled systems, preloading is usually done slowly using crosshead or actuator displacement feedback for controlling the test speed. Controlling preloading from load, stress, or strain feedback is not recommended as it could lead to undesirable and rapid acceleration until the specimen is pulled tight in the grips.
Depending on the amount of system compliance or slack that was taken up (reduced) during the preload, it may be necessary or desirable to zero the strain measurement at the end of preloading. However, caution must be taken so as to not adversely affect the overall strain measurement. In either case, test results that rely on strain from the extensometer should be adjusted so any non-linear behavior at the very beginning of the test curve does not adversely affect any test results.
Elastic Region
The elastic region or straight line portion of the test as seen on the stress-strain plot can often exhibit some non-linear behavior initially due to further straightening of the rebar specimen. If using an extensometer, this may show up as slightly negative strain at the beginning of the test and is generally considered normal for rebar.
When testing according to ASTM A615, the latest edition of ASTM A370 should be referred to for proper test control and target speeds permitted in the elastic region and until the onset of yielding.
When running the tests on servo-controlled systems, it is important to keep the following scenarios in mind. If using crosshead or actuator displacement control it is generally acceptable to use the same control and speed through both the elastic and yielding portions of the test. However, if stress or strain feedback control is used, the test must switch to crosshead or actuator displacement control just prior to or at the onset of yielding.
Yielding
Once yielding begins, many rebar grades exhibit a defined yield point that is seen as an abrupt bend in the stress-strain test curve. It is then followed by a period of specimen elongation with little to no increase in force. Because of this, servo-controlled systems must be controlled using crosshead or actuator displacement feedback in order to maintain a constant rate of travel throughout yielding. It is very important to note that using stress control during yielding will cause the test to accelerate excessively, which is in direct violation of the standards. This can also cause the yield point (upper yield) to be masked or smoothed and cause yield strength results to be higher than expected. Likewise, strain control from an extensometer can also become erratic during yielding and is therefore not recommended when testing rebar.
Plastic Region
As permitted by ASTM A370 and thereby ASTM A615, it is acceptable for the test speed to be increased after yielding has completed. For servo-controlled machines, the best way to control the test during this final region is from crosshead or actuator displacement feedback (same as yielding). However, the speed can be increased according to the standard being followed. This allows for the test to complete in a shorter period of time while still producing acceptable and repeatable results.
Broschüre Serie 6800 Premier Testing Systems
Universal-Testsysteme der Instron Serie 6800 bieten unvergleichliche Genauigkeit und Zuverlässigkeit. Die 6800 Serie basiert auf einer zum Patent angemeldeten Operator-Protect-Systemarchitektur mit einem brandneuen Smart-Close Air Kit und Collision-Mitigation-Funktionen, wodurch Materialtests einfacher, intelligenter und sicherer sind als je zuvor.
Broschüre Bluehill Universal
Bluehill Universal wurde von Grund auf für haptische Interaktion und eine intuitive Benutzererfahrung ausgelegt. Entdecken Sie einfacheres und schnelleres Prüfen mit Funktionen wie vorgeladene Prüfmethoden, QuickTest in Sekunden, verbessertem Datenexport und Instron Connect, einer neuen Funktion, die eine direkte Verbindung zum Service bereitstellt. Benutzer früherer Versionen von Software wie Bluehill 2 und Bluehill 3 können leicht auf die neueste Version von Bluehill aufrüsten.
Broschüre zu universellen Hochleistungs-Prüfmaschinen
Zu den Hochleistungs-Systemen von Instron gehören elektromechanische und hydraulische Prüfsysteme mit hoher Kapazität für Anwendungen mit Spannung und Kompression. Kraftkapazitäten reichen von 100 kN bis 2000 kN.
Hydraulisches seitlich wirkendes Spannzeug (DuraSync)
Instrons hydraulisches seitlich wirkendes Spannzeug ist für Hochleistungs-Tests konzipiert und hält auf der Probe eine konstante Spannkraft bei, die senkrecht zur Richtung der Prüfung wirkt und unabhängig von Zugbelastung ist.
2743-401 Hydraulische Keilzugspannzeuge
Die hydraulischen Keilzug-Spannzeuge von Instron mit 100 kN bieten eine innovative Lösung für Tests und Ergebnisse mit hoher Kapazität zur Verbesserung der Greifleistung, Benutzerfreundlichkeit und Bedienersicherheit.
Extensometer mit automatischem Kontakt – Modell AutoX 750
Das AutoX 750 ist ein hochauflösendes, langes, automatisches Kontakt-Extensometer. Es kann auf jeder elektromechanischen 3300-, 3400, 5500-, 5900- oder 6800-Tischplatte und entsprechenden Bodenmodell-Systemen sowie auf den statisch-hydraulischen Prüfsystemen LX, DX, HDX und KPX montiert werden. Es eignet sich hervorragend für Anwendungen mit Kunststoffen, Metallen, Biomedizin, Verbundwerkstoffen, Elastomeren und mehr. Das AutoX hat eine maximale Weglänge von 750 mm und eine Genauigkeit von ± 1 µm.